Sipco PU interior

Two pack, air drying, acrylic aromatic polyurethane coating for metal, wooden and plastic surfaces.
Features:

Excellent finish with high gloss
Excellent gloss retention & durability
Excellent flow & leveling properties
Excellent toughness & highly abrasion resistant
Excellent solvents, chemicals & lube oil resistance

Areas of application

All metal, plastic & wooden surfaces.

Caution:

In case of part mixing, which normally should be avoided, close the container lids tightly to avoid contact with moisture.
Inhalation of solvent vapors and contact of liquid with skin or eyes should be avoided where possible.
Even when ventilation is provided, respiratory, skin & eye protection wear are always recommended while spraying.

Click here to download information sheet

Sipco Hi Gloss PU Clear, Interior

Gloss	Hi Gloss
Recommended dry film thickness	20-30 microns
Recoatability	3-4 hours
Viscosity of the mix	32-40 seconds at 30 deg. C by Fc-4
Theoretical Coverage	Approx 10-12 sq.mtr/ltr at 20 microns
Drying time at 30 deg.	Surface dry 20-30 min Hard dry 5-6 hours max
Pot life	4 hours maximum
Flash Point	Base above 24 deg C
Shelf life	Minimum 12 months
Surface Conditions	Dry & free from all surface contaminations temperature range of the substrate: 4 deg. C to 50 deg C
Mixing	Mix hardener gradually into the base under continuous stirring, add only Sipco T-101 PU thinner if required.
Induction Time	15-20 minutes
Application	By Air Spray
Thinner	T-101 PU Thinner
Quantity of thinner to be used	10-25 %